Yazar "Bideci, Alper" seçeneğine göre listele
Listeleniyor 1 - 5 / 5
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Analysis of shrinkage and creep behaviors in polymer-coated lightweight concretes(Walter De Gruyter Gmbh, 2016) Bideci, Alper; Bideci, Ozlem Salli; Oymael, Sabit; Yildirim, HasanThe creep and shrinkage properties of polymer-coated lightweight concretes were examined. Five-hundred-dose lightweight concretes were produced by coating pumice aggregates with three different polymers (Sonomeric1: SNMC, KB Pur 214: KBP, and Polipol3455: PLP). The 3-, 7-, and 28-day compressive strength values of the obtained lightweight concrete samples were determined, and the 840-h and 12-month creep and shrinkage deformations were measured. It was found that the ductility of the SNMC- and KBP-coated concrete samples increased, while their shrinkage deformation results decreased when compared with the control samples. In contrast, the ductility of PLP concrete samples decreased and the shrinkage deformation became higher. In conclusion, the use of SNMC- and KBP-coated pumice aggregates had a positive effect on the creep and shrinkage properties of the concrete. Furthermore, it was observed that the compressive strength values of the lightweight concretes made of the coated samples were higher than those of the control sample.Öğe Diatomit Hammaddesinin Tuğla Üretiminde Kullanılabilirliğinin Araştırılması(Trakya Üniversitesi, 2008) Bideci, Alper; Bideci, Özlem SalliBu çalışmada, diatomit hammaddesinin tuğla üretiminde kullanılabilirliği araştırılmıştır. Bunun için Ankara İmrahor Bölgesindeki tuğla fabrikalarından alınan tuğla kili ve Ankara Şeker Fabrikası diatomit tesislerinden alınan diatomit hammaddesi kullanılmıştır. TSE 705 standardında verilen dolu tuğla sınıfı, (1.8/100) tuğlanın mekanik özellikleri göz önüne alınarak, farklı karışım oranlarındaki deney numuneleri, 800 °C, 900 °C ve 1000 °C 'de pişirme sıcaklıklarında pişirilmiştir. Uygun tuğla üretimi için, pişirilen deney numuneleri üzerinde standart testler uygulanmıştır. Deneysel çalışmalar sonucunda %20 diatomit katkılı ürünlerin 900 °C 'de pişirilmesi ile gerekli mekanik özellikleri sağlayan ürün elde edilebileceği görülmüştürÖğe Internal structure examination of lightweight concrete produced with polymer-coated pumice aggregate(Elsevier Sci Ltd, 2013) Bideci, Alper; Gultekin, Ali Haydar; Yildirim, Hasan; Oymael, Sabit; Bideci, Ozlem SalliIn the construction sector, pumice is observed to be used in both structural and non-structural building elements. In this study, to produce a new kind of concrete, the aggregates are coated with three different polymers (Sonomeric1 : SNMC, KB Pur 214: KBP and Polipol3455: PLP) that have multiple uses. The mineralogical-petrographical features of both polymer-coated and uncoated aggregates were examined, and SEM (Scanning Electron Microscope) and XRD (X-ray Diffraction) analyses were performed. Moreover, in the study, lightweight concrete elements with different dosages (300, 400 and 500) were produced by using polymer-coated and uncoated aggregates; and their internal structure examinations were performed and compressive strength values of 3, 7 and 28 days samples were investigated. As a conclusion; among the aggregate samples, it was determined that PLP-coated aggregates have a more porous structure than the other polymer-coated aggregates and KBP-coated aggregates could be used in lightweight concrete (500 dosage) production. It was also concluded that the compressive strength values of lightweight concrete elements produced with coated samples increased even more. (C) 2013 Elsevier Ltd. All rights reserved.Öğe Polimer kaplı pomza agregalarla elde edilen betonların özelliklerinin araştırılması(Trakya Üniversitesi Fen Bilimleri Enstitüsü, 2011) Bideci, Alper; Oymael, SabitPomza, volkanik faaliyetler sonucu oluşan; gözenekli, doğal kökenli hafif bir kayaç türüdür. Volkanik kaynaklı olan bu kayaçların pomza, perlit ve benzeri çeşitleri vardır. Ülkemizde özellikle inşaat sektöründe kullanımı giderek artmakta ve önem arz etmektedir. Üretim açısından kolay bir ürün olan pomza, ekonomik ve ayrıca ülke ekonomisine katma değeri yüksek olan bir malzemedir. Düşük birim ağırlık, ısı yalıtım özelliği, yangına karşı direnç gibi özelliklerinden dolayı tercih konusu olan hafif agregalı betonun, çağımızın popüler malzemesi olan polimerin su itme ve esneklik özelliği ile birleştirilerek farklı bir beton agregası ve beton üretimi, çalışmanın esasını oluşturmaktadır. Çalışmada çok yönlü olarak kullanılan polimerler ile pomza agregası kaplanarak elde edilen agregalar üzerinde, granülometri, özgül ağırlık, gevşek birim ağırlık deneyleri yapılmıştır. Üretilen bu agregalar ile hazırlanmış beton numuneleri üzerinde çökme, birim ağırlık, kuru birim ağırlık, basınç dayanımı, yarmada çekme dayanımı, su emme, dona dayanım, sünme ve rötre deneyleri gerçekleştirilmiştir. Araştırmada ayrıca agreganın çimento ile aderansı, SEM ve XRD ile mineralojik ve petrografik analizleri yapılarak sonuçlar yorumlanmıştır. Böylece agregaların polimer kaplanmasıyla su emmeleri azaltılarak, yeni bir agrega ve beton türünün üretimi gerçekleştirilmiştir.Öğe Polymer coated pumice aggregates and their properties(Elsevier Sci Ltd, 2014) Bideci, Ozlem Salli; Bideci, Alper; Gultekin, All Haydar; Oymael, Sabit; Yildirim, HasanPumices which are preferred due to their properties such as low unit weight, heat insulation property, resistance against fire were combined with polymer, the material of our age, to produce light concrete aggregate. In the study, pumice aggregate was coated by some polymers which are used for various purposes (Sonomeric1: SNMC, KBPur 214: KBP and Polipol3455: PLP) and the inner-structure examinations of the obtained aggregates was made by microscope and also specific weight, loose unit weight and water absorption experiments were applied. At the end of the study, the properties of pumice aggregates having high water absorption capability were developed and light aggregate production was realized. (C) 2014 Elsevier Ltd. All rights reserved.